API 5L X52 PSL 1 / API 5L X52 PSL 2 Pipes
API 5L X52 PSL 1 Seamless Steel Pipes, API 5L X52 PSL 2 Seamless Pipes, API 5L Seamless Pipes Suppliers
As an acclaimed enterprise of the industry, Reliable Pipes & Tubes is involved in offering a vast array of API 5L X52 PSL 1 / API 5L X52 PSL 2 Pipes as a manufacturer, exporter, stockiest and supplier to our domestic and global clients. API 5L X52 Pipe are used in offshore and onshore oil and gas pipelines requiring critical service, tight tolerances and high performance.
API 5l Welded Pipes, API 5l Psl 2 welded Pipe Exporter, API 5L X52 PSL 2 Welded Pipes Supplier Manufacturers Exporters.
ERW Pipes Manufacturer, SAW Pipes, LSAW Pipes Supplier, API 5l Pipes stockist, Exporter
Moreover, particular attention is given to toughness and toughness tests for sour services and higher pressure & temperature classes in these API 5L X52 PSL 2 Pipes. With respect to national and international quality of raw materials, we also offer these pipes in customized sizes and thicknesses as per specific demands by our esteemed clients at market leading prices.
API 5L X52 PSL 1 / API 5L X52 PSL 2 Seamless Pipes Specifications
Standard : API
Sizes LSAW/DSAW : 16'OD TO 54' OD (8 MM TO 50 MM THK)
Sizes (SAW) : 16” NB - 100” NB
Sizes (ERW) : 1/2” NB - 24” NB
Sizes (Seamless) : 1/2” NB - 60” NB
Wall Thickness : SCH10,SCH20,SCH30,STD,SCH40,SCH60,XS,SCH80,SCH100,SCH120,SCH140,SCH160,XXS DIN, JIS standard thickness
Dimensions : All Pipe is manufactured and inspected/tested to the relevant standards including ASTM, ASME, API.
Chemical Composition
Element | API 5L X52 PSL 1 / API 5L X52 PSL 2 |
C | 0.28 |
Mn | 1.20 |
P | 0.030 |
V | c,d |
NB | c,d |
Ti | d |
• 0.50% maximum for copper, 0.50% maximum for nickel, 0.50% maximum for chromium, and 0.15% maximum for molybdenum.
• For each reduction of 0.01% below the specified maximum concetration for carbon, an increase of 0.05% above the specified maximum concentration for manganese is permissible, up to a maximum of 1.65%
• Unless otherwise agreed, the sum of the niobium and vanadium contents shall be ≤0.06%.
• The sum of the niobium ,vanadium and titanium concentratons shall be ≤0.06%.
• Unless otheriwse agreed.
• Unless otherwise agreed, the sum of niobium, vanadium and titanium concentrations shall be ≤ 0.15%
Mechanichal Properties
Y.S | T.S | ELONGATION |
Mpa(psi) | Mpa(psi) | |
min | Min | min |
360 (52 200) | 460 (66 700) | 28% |