API 5L X56 PSL 1 / API 5L X56 PSL 2 Pipes
ERW Pipes Manufacturer, SAW Pipes, LSAW Pipes Supplier, API 5l Pipes stockist, Exporter
As an acclaimed enterprise of the industry, Reliable Pipes & Tubes is involved in offering a vast array of API 5L X56 PSL 1 / API 5L X56 PSL 2 Pipes as a manufacturer, exporter, stockiest and supplier to our domestic and global clients. API 5L X56 Pipe covers seamless and welded steel line pipe. It includes plain-end, threaded-end, and belled-end pipe, as well as through-the-flowline (TFL) pipe, and pipe with ends prepared for use with special couplings.
API 5l Welded Pipes, API 5l Psl 2 welded Pipe Exporter, API 5L X56 PSL 2 Welded Pipes Supplier Manufacturers Exporters.
 |
 |
API 5L X56 PSL 1 Seamless Steel Pipes, API 5L X56 PSL 2 Seamless Pipes, API 5L Seamless Pipes Suppliers
With respect to national and international quality of raw materials, we also offer these API 5L X56 PSL 2 Pipes in customized sizes and thicknesses as per specific demands by our esteemed clients at market leading prices.
API 5L X56 PSL 1 / API 5L X56 PSL 2 Seamless Pipes Specifications
Standard : API
Sizes LSAW/DSAW : 16'OD TO 54' OD (8 MM TO 50 MM THK)
Sizes (SAW) : 16” NB - 100” NB
Sizes (ERW) : 1/2” NB - 24” NB
Sizes (Seamless) : 1/2” NB - 60” NB
Wall Thickness : SCH10,SCH20,SCH30,STD,SCH40,SCH60,XS,SCH80,SCH100,SCH120,SCH140,SCH160,XXS DIN, JIS standard thickness
Dimensions : All Pipe is manufactured and inspected/tested to the relevant standards including ASTM, ASME, API.
Chemical Composition
| Element | API 5L X56 PSL 1 / API 5L X56 PSL 2 |
| C | 0.28 |
| Mn | 1.20 |
| P | 0.030 |
| V | c,d |
| NB | c,d |
| Ti | d |
• 0.50% maximum for copper, 0.50% maximum for nickel, 0.50% maximum for chromium, and 0.15% maximum for molybdenum.
• For each reduction of 0.01% below the specified maximum concetration for carbon, an increase of 0.05% above the specified maximum concentration for manganese is permissible, up to a maximum of 1.65%
• Unless otherwise agreed, the sum of the niobium and vanadium contents shall be ≤0.06%.
• The sum of the niobium ,vanadium and titanium concentratons shall be ≤0.06%.
• Unless otheriwse agreed.
• Unless otherwise agreed, the sum of niobium, vanadium and titanium concentrations shall be ≤ 0.15%
Mechanichal Properties
| Y.S | T.S | ELONGATION |
| Mpa(psi) | Mpa(psi) | |
| min | Min | min |
| 390(56 600) | 490(71 100) | F |